Product Name:Hight Temperature Kapton Tape Label
Backing: Polyimide film
Polyimide Film thickness:0.025mm
1.0-280℃ temperature resistance: put in 280℃ solder 5mintues,no fall off, no out of shape,;resist kinds of chemical erosion, wear and tear;keep the quality stability;meet the international standards in lead-free industrial processes;
2.Apply to the top of SMT process
3.Apply to heat transfer printing technology
4.Comply with ROSH standard
Used in printed circuit board,main board,the mobile phone’s high temperature tag;
anti counterfeiting trademakr;hight grade lighting printing trademark, etc...
Recomended Color bar:
Recomended to use RICOH-D110A /RICOH-B115C/RICOH-B110CRseries heat transfer ribbon
Zebra series printer or DATA MAX-1-4308 series printer
Polyimide film thickness
PASTE TO STAINLESS STEEL
PASTE TO EPOXIDE PC BOARD
180° Peel adhesion
Longation at break
Keep dry,avoid sunshine ,keep
Product Performance Data（Physical Performance）
Test method: use Zebra type printer or DATA MAX-1-4308 type printer and RICOH-D110A carbon or ROCOH-B110CR carbon at the concentration of 25 print sample labels.Before testing ,the sample is placed on the plate steel stainless and allowed to be placed for 24 hours.
Typical test results
5 minutes under 280º C（536º
No effect in 280º C,the label color slightly
seconds, ,do not fall
deformed the label performance no effected.
No effect in 220º C，A little color change in 240º C,
2 hours under 220º C（428º F）
in 260º C label, Serious color
change in 300º C, but no effected in performance.
No effect in 150ºC，a little color change in 185ºC，
1000 hours Under 150ºC（302ºF）
in 210º C, but no
1000 hours under -70ºC（-94ºF）
1000 hours in relative humidity
No effect, but the surface fade to light yellow
As American test and materials
association ASTM G26 test,1000
hours under inan arc xenon
Spray 5% salty liquid into mist
shape in laboratory, and put
the label in laboratory 30
days.(ASTM B 117)
Heat Resistance/Scrap Resistance/ChemicalTest:
Test method:use Zebra type printer or DATA MAX-1-4308 type printer and RICOH-D10A carbon or ROCOH-b110CR carbon at the concentration of 25 print sample labels.Print content is 3:1,the most narrow strip width is 6mil bar code.Test enviroment listed as below.
Conflict print effect
Heating 5minutes in
trichloroethane in 74ºC
10mintues in 30%
Aquanox SSA-TM water
terpene in 40~45ºC
terpene in 40~45ºC
2110 saponifier with 6%
water,produced by Alpha
Metals company in
10 minutes in 99%
isopropanol in 82ºC
10 minutes in 100ºC ion
Print effect compare:
1.Compared with Quick Check 500B (aperture:0.005",Wave length:660m),produced by Photographic Sciences company.
2.Read Rate:The scan result by Intermec-®1621canner.
3. saponifier:soak 2minutes in 100ºC ion water
If the high tempetraure polyimide film adhesive tape label caters to your requirement, please be free to buy the quality products made in China with our professional manufacturers and suppliers in China. We're equipped with a productive factory at your service.